Silane Crosslinked Halogen Free Low Smoke Flame Retardant Polyolefin Cable material For Power Storage System

Silane Crosslinked Halogen Free Low Smoke Flame Retardant Polyolefin Cable material For Power Storage System

Description

The product suitable for the insulation and sheath layer of electromagnetic connection wire used in power storage system, which is safe and environmental protection material, meets RoHS,REACH standard.

Application

Performance

Use Methods

1. Mixing: Mix the Component A and Component B evenly, add them into the hopper. If the color required, use the EVA base materials (the color masterbatch should be dried). The material should be use up within 2 hours after unpacking.(It can’t be dried.)The external water can’t be brought in during the process. 

2. Screw Type: Compression Ratio：1.5±0.2 

3. Extrusion Temperature：

Control the melt temperature at 160±10℃. The extrusion temperature should be adjusted according to the actual situation.

4. Pay-off Speed: Without the effect of smoothness and performance, the faster is better. 

5. Cross-linking: The crosslink of the cable: Natural crosslink or Water bath(Steam). Natural Crosslink: Temperature 15-25℃,crosslink will be finished around 7days.When temperature is higher than 25℃,crosslink will be finished around 3days.Water bath or Steam:should control the temperature around 60℃in order to keep it from sticking together,it will finish about 4hours. The thickness of the test piece is 1mm. If thickness >1mm,the crosslink time should be adjusted according to actual situation.Full performance test, water bath (steam) 60 ℃, more than 8 hours, to ensure the material is fully crosslinked.

Package, Transport and Storage 

Package：Vacuum packed. Transport: Can’t be exposed to the sun or rain, or suffer mechanical damage. Storage：Should be stacked on the pallet in a clean, dry and ventilated warehouse. Warranty：6 months.